Amandla aphezulu kune-alumina
Izindleko eziphansi kunezirconia
Ukumelana nokugqoka okukhethekile
Ukumelana nokugqwala okuphezulu
Ukuqina kwe-fracture ephezulu
Ukuqina kwezinga lokushisa eliphezulu
Amalayini e-ceramic angavimbeli ukugqoka asetshenziselwa ukunikeza ukuguga okuphezulu nokuvikelwa komthelela.
1) Hlanganisa irabha emunca amandla kanye ne-abrasion ephezulu ekwazi ukumelana ne-alumina ceramic, ilungele ukuguga okuphezulu kanye nezicelo ezinomthelela.
2) Umumo nosayizi wangokwezifiso ukuze uhlangabezane nezidingo zakho ezithile, amalayini ajwayelekile kanye nalawo angajwayelekile ayatholakala.
3) Izixazululo eziphelele zokuguga nokuhuzuka
4) Umkhiqizi onokuhlangenwe nakho okucebile, isibopho esihle phakathi kwerabha ne-ceramic, izitsha zobumba zihlala endaweni zize ziguge ngokuphelele.
5) Uhlu olubanzi lwamapuleti okugqoka erabha e-ceramic ukuhlangabezana nezidingo zakho ezahlukene.
1) Indlu
2) Phakamisa i-chute
3) Khipha i-chute
4)Isitoreji se-ore
5) Iqhwa
6) Umgqomo
INGXENYE | IZIMPAHLA | I-UNIT | I-ZTA Ceramic |
I-Ceramic | I-Al2O3 | % | 70-75 |
ZrO2 | % | 25-30 | |
Ukuminyana | g/cm3 | 4.20 | |
Vickers ubulukhuni | Kg/mm2 | 1300 | |
Ukuqina kokuphuka | Mpa.M1/2 | 3-4 | |
Irabha | Amandla e-Flexural | Mpa | 680 |
Ukwakheka | - | Irabha yemvelo+SBR | |
Ukuqina kogu | HA | 60±5 | |
Isilinganiso sobude obuqinile | % | >400 | |
Amandla aqinile | Mpa | 25 | |
Amandla wezinyembezi(%) | % | 30 | |
Amandla okubopha phakathi kwerabha ne-ceramic | Mpa | 4 | |
Insimbi | Okubalulekile | - | Q235A |
Amandla okuqina Ukuminyana | g/cm3 | 7.85 | |
Ubukhulu | mm | 5-6 | |
Okunamathelayo | Ukubukeka | - | Uketshezi olunamanzi ansundu |
Okuqukethwe okuqinile | - | 20±3% | |
I-Viscosity | Mpa | ≥2.5 | |
Amandla e-peel | 48h N/2.5cm | ≥120 | |
Amandla acindezelayo | Mpa | ≥850 | |
Izinga lokushisa lokusebenza | ºC | - 20 - 100 |
Samukela ama-oda angokwezifiso.
Uma ufuna ukwazi ulwazi oluthe xaxa lomkhiqizo, sicela ukhululeke ukuxhumana nathi futhi sizokukhokhela umkhiqizo ofaneleka kakhulu kanye nenkonzo engcono kakhulu!